The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
（2）高温調整と極低温処理の後、溶液を最初に950度に90分間加熱します。 Msポイントの上昇により、室温まで冷却することで少量のマルテンサイトを得ることができます。 マルテンサイトの量。
（3）冷間変形法による溶体化処理後、室温で冷間変形を行います。 冷間変形中に904Lシームレスパイプに形成されるマルテンサイトの量は、変形量と904Lステンレス鋼パイプの組成に関係しています。
上記の3つの方法は、ステンレス鋼管の溶体化処理に一般的に使用される方法です。 彼らがあなたを助けてくれることを願っています。